Manganese carbonide is a stable, manganese-carbon-based compound. Mn3C has the chemical formula and the melting point at about 1520degC. Its density is 6.89g/cm3.
Particle Size: -325mesh
About Manganese Carbide Mn3C Powder:
It is made from carbon and manganese.
What is Mn3C?
It is approximately 1520degC
6.89 g/cm3. Manganese carbide burns quickly in oxygen, and is decomposed in water to make manganese hydrogenxide and methane. It can be easily reduced to acid, decomposed by chlorine or fluorine, and further decomposed into carbon and manganese at very high temperatures.
The heat of the formation of manganese carbide is ^fHm (298K)=-(15.06+-12.55)kJ/mol. The result of smelting manganese-silicon or high-carbon ferromangannese in an electric furnace or blast furnace is manganese carbide. This means that the reaction absorbs less heat than reduction to metallic manganese and manganese siliicide. It starts
It is cold. The high-carbon ferromanganese is therefore more carbon.
To receive the most current information, send us an inquiry
Please fill out the form below if you wish to
buy Manganese Carbide Powder
Manganese Carbide Mn3C powder performance:
It is simple.
Manganese Carbide Mn3C Powder
Mn3C has the following physical characteristics: Mn3C is a hard crystalline solid, or bright needle crystal. Its relative density is 6.89. Concentrated sulfuric acid or nitric Acid will insoluble it, however, water or dilute acids can decompose it to create manganese hydroxyide, hydrogen, and other hydrocarbons. It is easily reacted with fluorine or chlorine, and it burns fast in oxygen.
Technical Parameters of Manganese Carbide, Mn3C Powder
Certificate for Mn3C powder
Get carbon free
Size for Particel
The gas-based reduction manganese oxide is a method of making manganese carbide. Once you have mixed manganese dioxide, water, and binder together, the dry block can be placed in an atmosphere with H2, CO, CO, and N2. Then, it is calcined at 1100 1300, which is manganese carbide. Here are the specific steps. The mass percent of -325 mesh size refers to 90% analytically purified manganese dioxide, trimanganese troxide and mixed with 0.5% CMC. Finally, pelletization and drying take place. After drying, the sample is placed in an atmosphere of 10% CMC, 30% H2, 10% CO and 50% Nitrous Oxide at 1150degC. The calcination process takes 120 minutes. After cooling down to room temperature the obtained manganese carbide product can be converted into manganese dioxide at 95%.
Manganese Carbide Mn3C Powder:
Manganese carbonide Mn3C powder can be used to make hard coatings, target, weld materials, and spray tools. It is also used in the steelmaking industry, aerospace, and many other areas.
The grain refiner of Cermet and Wolfen carbide, manganese carbonide has the ability to significantly enhance the properties of an alloy.
Manganese troxide is an important raw material in the manufacture of soft magnetic materials of manganese, zinc ferrite and other electronic materials. This is why it is so widely used.
To prepare transformer oils, you can use manganese carbonide. This is a simple process that can be easily replicated on large scales.
Manganese Carbide, Mn3C powder storage conditions:
Manganese Carbide, Mn3C Powder, should be maintained in a dry, cool, and sealed environment.
Shipping and Packing of Manganese Carbide 3C Powder
You can pack it in two plastic bags with the inside.
Manganese Carbide Mn3C Powder packing: vacuum packing, 100g, 500g or 1kg/bag, 25kg/barrel, or as your request.
Manganese Carbide Mn3C Powder shipping:
Could be sent by express or by sea after receipt of payment.
Jatujakguide advanced materials Nano Technology Co. Ltd., (Jatujakguide), is a reliable global supplier and manufacturer. They have over 12 years of experience in manufacturing super-high quality chemicals and Nanomaterials. This includes boride, nitride, graphite, sulfide, 3D printing powders, as well as boride, nitride, and graphite powders.
Send us an enquiry if you're looking for Manganese Carbide Powder of high quality. (